ABSTRACT Background: Blended paper can present suitable mechanical properties due to sirnergetic effect. However, regarded to physical properties, few studies are conducted. This study aimed to evaluate optical, structural, interfiber bonding, and other physical properties from blended paper and try to understand how these properties can affect applications. The eucalyptus, sisal, and pine pulp were used for handsheet forming. Pulps were disintegrated, refined, and blended two by two in 5/95%, 25/75%, and 45/55% ratios. Also, virgin pulps (100% of each pulp) were used for handsheet forming. Handsheets were formed and evaluated by bond strength, cobb test, air permeance, roughness, optical, Fourier transform infrared spectroscopy (FTIR), and scanning electron microscopy (SEM). Results: Treatments differed statistically in bond strength, cobb test, optical, air permeance, and roughness. Generally, treatments with eucalyptus presented higher bond strength, brightness, and air permeance. Treatments with sisal presented the highest opacity and roughness. Spectra of virgin handsheets presented differences in 2170-2000 and 2360 cm-¹ bands, probably related to residual lignin content. SEM images revealed structural differences between blended and virgin pulps. Conclusion: Treatment T15 (45S 55P) presented the best results, suggesting better physical-mechanical properties. Blended handsheets presented better properties than virgin handsheets on most properties, evidencing a synergetic effect.

RESUMO Neste trabalho, o resíduo fuligem de candeia foi utilizada para obter carvão ativado. A ativação foi investigada utilizando três reagentes (NaOH, H3PO4 e CO2). Os resultados de análise térmica e microscopia eletrônica de varredura mostram que os carvões ativados possuem maior estabilidade térmica e partículas mais regulares e menores quando comparados ao precursor. Medidas de área superficial mostraram que os carvões ativados com NaOH e CO2apresentaram resultados iguais a 804 e 435 m2g-1, respectivamente, e maior capacidade para adsorver o azul de metileno (222 e 118 mgg-1, respectivamente). Os valores de capacidade de adsorção são cerca de 10,6 e 5,6 vezes maiores para os carvões ativados em comparação à capacidade de adsorção da fuligem. Os resultados demonstram o grande potencial de se obter carvão ativado a partir de fuligem residual.

ABSTRACT In this study, candeia soot waste was used for the production of activated carbons. Activation was investigated using three reagents (NaOH, H3PO4 and CO2). The results of thermal analysis and scanning electron microscopy show that the activated carbons present higher thermal stability and more regular and smaller particles when compared with the precursor. Surface area measurements showed that NaOH and CO2 activated carbons present higher specific surface areas (804 and 435 m2g-1, respectively) and higher abilities to adsorb methylene blue (222 and 118 mgg-1, respectively). The adsorption capacity values of the activated carbons are nearly10.6 and 5.6 times higher than the value found for the candeia soot residue. The results demonstrate the great potential of obtaining activated carbons from residual soot.

ABSTRACT Activated carbons (AC) are high porosity and adsorptive carbonaceous materials. These adsorbents can be produced using different organic materials. Precursor material properties may impact their quality. This study aimed to produce activated carbon from Tectona grandis wood wastes, besides determining efficiency in adsorption of different pollutants. Chemical activation, with ZnCl2 (AC_ZnCl2) and CuSO4 (AC_CuSO4), and physical activation, with CO2 (AC_CO2) were performed. Activated carbons were characterized by FTIR, surface functional groups (Boehm) and surface area analysis. Moreover, ACs were tested regarding adsorption capacity of methylene blue (MB), phenol and Cr+6 ions in aqueous medium. Higher total pore volume (0.62 cm³ g-¹), micropore volume (0.31 cm³ g-¹) and surface area (524.50 m² g-¹) were obtained in AC_ZnCl2, which was also the most effective in MB and phenol adsorption. AC_CuSO4 obtained high adsorption capacity for phenol and presented functional groups different from the other AC. AC_CO2 was the second with better adsorption performance for all pollutants.

Surface modification may lead activated carbon (AC) to take on different properties. This study aimed to promote surface modification of activated carbons using corona treatment (electrical discharge). In this study, powdered commercial activated carbon was used. Activated carbons were subjected to corona treatment at different exposure times (2, 5, 8 and 10 min) at 4.5 cm height from the source. To observe differences promoted by treatment, activated carbons were analyzed by acidity, surface functional groups, Fourier Transform Infrared Spectroscopy (FTIR), elemental analysis (CHN), proximate analysis and thermogravimetry. Corona treatment impacted surface chemistry of activated carbons. There was a trend of increasing surface acidity according to exposure time. There were changes in functional groups, increasing carboxyl acid and decreasing lactone and phenol groups. FTIR analysis showed peaks in the bands at 3500, 1650 and 1300 cm-1. Increase of oxygen content and decrease of carbon content were also found. Immediate analysis followed similar tendency for volatile and fixed carbon content. There were also differences in thermogravimetry analysis. Treated activated carbons were different compared to virgin activated carbon. This difference was performed by surface oxidation. Thus, this study showed that corona treatment caused surface modifications and might impact adsorption process.

RESUMO O trabalho teve como objetivo verificar o efeito de diferentes doses de nitrogênio na produção de matéria seca e na qualidade da madeira e carvão vegetal de um clone híbrido de Eucalyptus grandis x Eucalyptus urophylla, aos 6 anos de idade. Foram analisadas 40 árvores, sendo estudados 5 tratamentos em 4 blocos e amostradas 2 árvores por tratamento dentro de cada bloco. Os tratamentos consistiram da aplicação de 0 kg, 60 kg, 120 kg e 240 kg.ha-1 de nitrogênio (N), como sulfato de amônio, com o objetivo de avaliar se a resposta ao sulfato de amônio era exclusivamente devida ao N. Foi aplicado ainda um tratamento adicional, com aplicação de 120 kg.ha-1 de N como nitrato de amônio, totalizando 5 tratamentos. Foram avaliadas as características de crescimento da árvore, densidade básica, estimativa de massa seca, composição química e energética da madeira e as características físicas, químicas e energéticas do carvão. Observou-se que a produção de massa seca tendeu a aumentar com a aplicação da dosagem de nitrogênio. O efeito da dosagem de nitrogênio não influenciou a densidade básica e as características energéticas do carvão vegetal, porém os teores de nitrogênio elementar, extrativos totais e lignina na madeira apresentaram aumento com a nutrição aplicada. A nutrição utilizada não influenciou as características químicas e energéticas da madeira e do carvão vegetal.

ABSTRACT The present work aimed to verify the effect of different dosages of nitrogen on the production of dry material, and wood and charcoal quality made from a six years old hybrid clone of Eucalyptus grandis x Eucalyptus urophylla. Overall 40 trees were analyzed and five treatments in four blocks were studied, with two trees sampled per treatment within each block. Treatments consisted in the application of 0, 60, 120 and 240 kg.ha-1 of nitrogen (N) as ammonium sulfate in order to evaluate if the response to such compound was exclusively due to N. An additional treatment was applied with 120 kg.ha-1 of N as ammonium nitrate, totalizing five treatments. The tree growth, basic density, dry mass estimate, chemical and energetic composition of wood were evaluated, as well as physical, chemical and energetic characteristics of charcoal. The production of dry mass tended to increase with the nitrogen dosage applied. The effect of nitrogen dosage did not influence the basic density and energetic characteristics of charcoal, however the content of elemental nitrogen, total extractives and lignin of wood increased with nutrition. Such application did not influence the chemical and energetic characteristics of wood and charcoal.

RESUMO A degradação de corantes é um importante tópico nas ciências ambientais, já que os corantes podem trazer diversos problemas para o meio ambiente. O carvão ativado é um importante material usado como adsorvente dessas substâncias causadoras dos mais diversos danos, mas precisam ser melhoradas especialmente quando envolve substâncias específicas. Este manuscrito tem como objetivo avaliar o impacto da superfície de carvões ativados modificados pelo tratamento corona (descarga elétrica) na adsorção de diferentes corantes. Os carvões ativados foram tratados pelo tratamento corona para promover a modificação na superfície, modificando os tempos de exposição ao tratamento (2, 5, 8 e 10 minutos). A avaliação da adsorção foi realizada pelas isotermas de adsorção e velocidade de adsorção. Os corantes diferiram pelas suas cargas (aniônico e catiônico) e massa molecular. Os corantes utilizados foram o Azul de Metileno (catiônico) e o Vermelho Congo (aniônico). A área superficial e a microscopia eletrônica de varredura (MEV) também foram realizadas. A superfície química foi impactada pelo tratamento corona e interferiu na adsorção dos corantes. Houve decréscimo na adsorção dos corantes para ambos de acordo com o tempo de exposição. No entanto, o decréscimo de Azul de Metileno (25%) foi maior que para o Vermelho Congo (14%), sugerindo que a carga ou a massa molecular interferiram na isoterma de adsorção. Na velocidade de adsorção, não houve nenhuma diferença entre os tratamentos, embora houve diferença no equilíbrio da adsorção. A análise MEV mostrou que a superfície foi impactada (destruição dos poros) pelo tratamento corona. Além disso, a área superficial estimada foi fortemente impactada pelo tratamento, reduzindo com o aumento do tempo de exposição. Assim, a propriedades texturais pode ter contribuído para a redução na capacidade de adsorção de ambos corantes, desempenhando papel de maior importância comparado com as propriedades químicas.

ABSTRACT Dye degradation is a significant topic in environmental science, since dyes can bring several problems to the environment. Activated carbon (AC) is an important material used as adsorbent of these hazardous substances, but need to be improved especially into specific substances. This paper aimed to evaluate the impact of activated carbon surface modified by corona treatment (electric discharge) on adsorption of different dyes. Activated carbons were treated by corona treatment to cause surface modification, modifying exposure time to treatment (2, 5, 8 and 10 minutes). Evaluation of adsorption was performed by adsorption isotherms and kinetic adsorption. Dyes differed in their charge (anionic or cationic) and molecular weight. Dyes used were Methylene Blue (cationic) and Congo Red (anionic). Surface area and Scanning Electron Microscopy (SEM) were also conducted. Surface chemistry was impacted by corona treatment and interfered in dye adsorption. There was decrease of dye adsorption for both dyes according to time exposure. However, the decrease of Methylene Blue (25%) was higher than Congo Red (14%), suggesting that either charge or molecule weight interfere in the adsorption isotherms. In kinetic adsorption, there was no difference between treatments, although there was a difference in adsorption equilibrium. SEM showed that surface was impacted (pore destruction) by corona treatment. Furthermore, estimated surface area was strongly impacted by the treatment, reducing with the increase of time exposure. Thus, textural properties might have contributed to reduce adsorption capacity of both dyes and play a higher role than chemical properties.

O processo de armazenamento de bebidas destiladas em barris de madeira é uma prática que visa à melhoria das características sensoriais da bebida, tais como cor, aroma e sabor. A qualidade da bebida destilada armazenada nesses barris depende de características da madeira como densidade, permeabilidade, composição química e anatomia, além do tipo de tratamento térmico dado à madeira durante a confecção dos barris. O Brasil possui uma grande diversidade florestal, principalmente no norte do país, na Amazônia. Essa região abriga milhares de espécies de árvores, porém, limita-se à utilização de pouco mais de duas espécies nativas e outras exóticas para o armazenamento de bebidas. Assim, objetivou-se, neste trabalho, determinar algumas das características físicas e químicas das madeiras de quatro espécies florestais da Região Amazônica. Os resultados obtidos para as espécies arbóreas aqui estudadas serão comparados com os de madeiras já utilizadas para o armazenamento de bebidas destiladas. As espécies estudadas foram angelim-pedra (Hymenolobium petraeum Ducke), cumarurana (Dipteryx polyphylla (Huber) Ducke), jatobá (Hymenaea courbaril L.) e louro-vermelho (Nectandra rubra (Mez) C.K. Allen). As árvores foram coletadas em área de manejo florestal da Empresa Precious Woods Amazon, em Silves, Amazonas. Dentre as análises realizadas foram determinados: teores de extrativos totais, quantidade de lignina, porcentagem de minerais (cinzas) e teores de taninos, além de densidade básica, análise elementar (CHNS-O) e análise térmica. Observou-se que a composição química estrutural (teores de lignina, holocelulose) e elementar (porcentagem de C, H, N e O) das madeiras possuem diferenças significativas. A madeira do jatobá possui maior teor de taninos e, na análise térmica, foi a madeira com menor perda de massa.

The process of storing liquor in wooden barrels is a practice that aims to improve the sensory characteristics, such as color, aroma and flavor, of the beverage. The quality of the liquor stored in these barrels depends on wood characteristics such as density, permeability, chemical composition, anatomy, besides the wood heat treatment used to fabricate the barrels. Brazil has a great diversity of forests, mainly in the north, in the Amazon. This region is home to thousands of tree species, but is limited to the use of only a few native species to store liquors. The objective of this study was to determine some of the physical and chemical characteristics for four Amazon wood species. The results obtained in this study will be compared with others from woods that are traditionally used for liquor storage. The species studied were angelim-pedra (Hymenolobium petraeum Ducke) cumarurana (Dipteryx polyphylla (Huber) Ducke), jatobá (Hymenaea courbaril L.) and louro-vermelho (Nectandra rubra (Mez) CK Allen). The trees were collected from Precious Woods Amazon Company forest management area, in Silves, Amazonas. Analyzes such as: concentration of extractives, lignin amount, percentage of minerals (ash) and tannin content, density, elemental analysis (CHNS-O) and thermal analysis were done. It was observed that the chemical composition (lignin, holocellulose) and elemental analysis (percentage of C, H, N and O) of the woods have significant differences. The jatobá wood presented higher tannin content, and in the thermal analysis, was that which had the lowest mass loss.

Foram estudadas madeiras de híbridos de Eucalyptus grandis x Eucalyptus urophylla em três diferentes idades. As características das madeiras e dos carvões produzidos, a partir dessas madeiras, bem como influência da madeira nas características dos carvões produzidos foram avaliadas. Foram realizadas análises químicas (extrativos, lignina, cinzas, análise elementar), densidade básica e poder calorífico superior - PCS nas madeiras. O carvão foi produzido em forno tipo mufla, com taxa de aquecimento 1,67 ºC.min-1 e temperatura final de 450 ºC. Para os carvões, foram realizadas análise imediata, análise elementar e rendimento gravimétrico do processo de pirólise. Foi observado um aumento nos valores de densidade, teor de extrativos, teor de carbono e relação C/H da madeira com a maturidade da árvore. Outras características como teor de cinzas e relação S/G tiveram seus valores diminuídos com a idade da árvore. Maior rendimento gravimétrico em carvão e em gases não-condensáveis foram encontrados no material mais maduro.

In the present studied was investigated hybrids of Eucalyptus grandis x Eucalyptus urophylla in three different ages. Wood and charcoal characteristics as well as the influence of wood characteristics on the charcoals produced were evaluated. Chemical analyzes (extractives, lignin, ash, elemental analysis), basic density and calorific value - PCS were performed for wood. The charcoals were produced in a muffle type furnace with a heating rate of 1.67 °C.min-1 and an end temperature of 450 °C. Volatile material content, ash content, fixed carbon content, elemental analysis and gravimetric yield of the pyrolysis process were performed for the charcoals. An increase in density values, extractives content, carbon content and C/H rate were observed with the maturity of the tree. Other features such as ash content and S/G ratio decreased with the age of the tree. Greater gravimetric yield in charcoal and non-condensable gases were found in more mature materials.

Foram estudadas madeiras de híbridos de Eucalyptus grandis x Eucalyptus urophylla, em três idades diferentes, com o objetivo de avaliar o comportamento da madeira e do carvão vegetal produzido diante do aumento controlado de temperatura, bem como verificar a influência das características da madeira sobre o carvão vegetal. Foram realizadas análises químicas (extrativos totais, lignina, holocelulose, celulose, cinza e análise elementar) e térmicas (análise termogravimétrica - TG, análise térmica diferencial - DTA e calorimetria 1,67 ºC min-1 e temperatura final de 450 ºC. No carvão vegetal produzido, foram realizadas análise imediata, elementar e térmica. A densidade básica da madeira correlacionou-se positivamente com a relação carbono/ hidrogênio (C/H) e negativamente com os teores de cinza, nitrogênio, oxigênio, enxofre e relação siringil/ guaiacil (S/G). Os teores de cinza, nitrogênio, enxofre e S/G da madeira correlacionaram-se positivamente entre si e negativamente com a variável C/H da madeira. O teor de carbono fixo (TCF), o poder calorífico do carvão vegetal, o teor de carbono elementar e a relação C/H correlacionaram-se positivamente entre si e negativamente com o teor de materiais voláteis (TMV). O teor de lignina correlacionou-se positivamente com o rendimento gravimétrico em carvão (RGC) e negativamente com o TCF.

Three different ages of . Eucalyptus grandis x . Eucalyptos urophylla wood hybrids were studied, with purpose of evaluating wood and charcoal behavior by temperature rising, and investigating the influence of wood characteristics on charcoal. Wood was analyzed chemically (total extractives, lignin, holocellulose, cellulose, ash and elementary composition) and thermally (thermogravimetry analysis - TG, differential thermal analysis - DTA and differential scanning calorimetry - DSC). Also, basic density and higher heating value were evaluated. Charcoal was produced in muffle furnace with constant heating rate of 1,67 ºC min-1 up to 450 ºC. In the produced charcoal, immediate analysis were conducted, elementary and thermal. The basic density of wood had positive correlation with C/H relation, and negative correlation with ash, nitrogen, oxygen, sulfur contents and S/G relation. The wood contents of ash, nitrogen, sulfur and S/G had positive correlation among each other, and negative correlation with C/H relation. In charcoal, the fixed carbon content, calorific value, elementary carbon content and C/H relation had positive correlation among each other, and negative correlation with volatiles content. The lignin had positive correlation with gravimetric yield in charcoal (RGC) and negative correlation with fixed carbon.

Este trabalho teve como objetivo avaliar a qualidade da madeira e do carvão vegetal de algumas espécies de ocorrência do cerrado mineiro visando o uso siderúrgico. Foram utilizadas cinco espécies de madeiras de ocorrência no cerrado procedentes do Estado de Minas Gerais. Na madeira foram avaliadas a densidade básica e os teores de lignina, extrativos totais, holocelulose e cinzas. No carvão vegetal foram avaliados os rendimentos em carvão vegetal e em carbono fixo, os teores de carbono fixo, materiais voláteis e cinzas, o poder calorífico superior e a densidade relativa aparente. Na avaliação do experimento utilizou-se o delineamento inteiramente casualizado com quatro repetições. Utilizou-se ainda a análise multivariada de componentes principais. As espécies Casearia sylvestris e Luehea divaricata apresentaram os maiores rendimentos gravimétricos em carvão vegetal e em carbono fixo, bem como elevados teores de lignina na madeira. O carvão vegetal da espécie Trema micrantha possui elevado poder calorífico superior, mas a menor densidade relativa aparente. A espécie Guazuma ulmifolia se destacou pelo elevado teor de carbono fixo e grande potencial para uso siderúrgico, juntamente com a espécie Casearia sylvestris.

The aim of this research was to evaluate the quality of wood and charcoal of some species from cerrado mineiro aiming the production of bioenergy and use in steel industry. Five wood species from cerrado located in Minas Gerais state were used. Basic density and lignin, total extractives, holocellulose and ash contents were evaluated. Charcoal and fixed carbon yields, contents of fixed carbon, volatile materials and ashes, higher heating value and apparent relative density were evaluated. An entirely randomized design with four repetitions was used in the evaluation of the experiment. Moreover, multivariate analysis of principle components was used. The species Casearia sylvestris and Luehea divaricata had the highest gravimetric yield of charcoal and fixed carbon, as much as high lignin contents in the wood. Charcoal made from Trema micrantha presented high heating value, but the lowest apparent relative density. The species Guazuma ulmifolia stood out due to high fixed carbon content and great potential for use in the steel industry, together with the specie Casearia sylvestris.

A serragem é um resíduo sólido, gerado na indústria madeireira, que não tem uso rentável e pode causar sérios problemas ambientais quando disposta inadequadamente. Neste estudo, objetivou-se utilizar a serragem de eucalipto na preparação de carvões ativados (AC) e testá-los como adsorventes do corante azul de metileno (MB) e fenol; moléculas que representam poluentes de efluentes industriais. A serragem de eucalipto foi caracterizada por análises instrumentais, tais como: análise elementar (CHNS-O), análise termogravimétrica (TGA), espectroscopia na região do infravermelho (FTIR) e microscopia eletrônica de varredura (SEM). Os carvões ativados foram preparados por ativação física com dióxido de carbono AC_CO2, (10º Cmin-1, 850ºC, 1h) e pela ativação química com carbonato de potássio- AC_K2CO3 (10º Cmin-1, 850º C, 3h). O AC_CO2 e AC_K2CO3 foram caracterizados por CHN-O, TGA, FTIR, adsorção/dessorção de N2 (área BET) para avaliar a área superficial específica e SEM. Os carvões ativados resultantes foram testados quanto à capacidade de adsorver MB e fenol na água. Os carvões produzidos apresentaram características de material microporoso, apresentando área superficial média de cerca de 535 m²g-1. O AC_K2CO3 foi mais eficiente na adsorção do MB (81mgg-1) e fenol (330mgg-1) que o AC_CO2 (32mg g-1 e 172 mg g-1, respectivamente, para MB e fenol).

Wood sawdust is a solid residue, generated in the timber industry, which is of no profitable use and can cause serious environmental problems if disposed inadequately. The aim of this study was to use the eucalyptus sawdust in the preparation of activated carbons AC) and test them as adsorbents of methylene blue (MB) and phenol, representative pollutants from aqueous effluents of various industries. The eucalyptus sawdust was characterized by instrumental analysis such as elementary analysis (CHNS-O), thermogravimetric analysis (TGA), infrared spectroscopy (FTIR) and scanning electron microscopy (SEM). The activated carbons were prepared by physical activation with carbon dioxide AC_CO2, (10º C min-1, 850º C, 1h) and by chemical activation with potassium carbonate AC_K2CO3 (10º C min-1, 850º C, 3h). The AC_CO2 and AC_K2CO3 were characterized by CHN-O, TGA, FTIR, N2 adsorption/desorption (BET) to evaluate the specific surface area and SEM. The resulting activated carbons were tested for their ability to adsorb MB and phenol in water. The activated carbons produced in this work were predominantly microporous and showed specific surface area of about 535 m² g-1. The AC_K2CO3 was more effective in the adsorption of MB (81 mg g-1) and phenol (330 mg g-1) than AC_CO2 (32 mg g-1 and 172 mg g-1, respectively, for MB and phenol).

A utilização de resíduos vegetais para fins energéticos já é uma realidade, porém, para afirmar e indicar um determinado material como bom gerador de energia, é necessário caracterizá-lo através de análises químicas e da determinação de seu valor calórico. Objetivou-se, com este trabalho, analisar diferentes resíduos de biomassa vegetal, caracterizando-os como potenciais para a produção de energia. Para a realização deste trabalho, foram utilizados os seguintes resíduos: resíduos do processamento da madeira (serragem e maravalha); pergaminho do grão e caule do cafeeiro; caule e vagem do feijão; caule e vagem da soja; casca de arroz; folha, caule, palha e sabugo de milho e palha e bagaço da cana-de-açúcar. Para a caracterização dos resíduos, foram realizadas as seguintes análises: análise química, análise química imediata, poder calorífico e análise elementar. Todas as análises foram conduzidas no Laboratório de Energia da Biomassa Florestal da Universidade Federal de Lavras. De forma geral, todos os resíduos apresentaram potencial para serem utilizados na produção de energia. A casca de arroz apresentou o maior teor de lignina, característica interessante para produção de energia. No entanto, o seu alto teor de cinza acarretou uma redução no poder calorífico e carbono fixo. Os demais resíduos apresentaram características semelhantes do ponto de vista energético, com destaque para o sabugo de milho, que apresentou maior poder calorífico, seguido do caule do café, ambos continham também maior quantidade de carbono e carbono fixo. O poder calorífico superior apresentou alta correlação com o teor de materiais voláteis, carbono e hidrogênio.

The use of plant residues for energy purposes is already a reality, yet in order to ensure suitability and recommend a given material as being a good energy generator, it is necessary to characterize the material through chemical analysis and determine its calorific value. This research aimed to analyze different residues from plant biomass, characterizing them as potential sources for energy production. For the accomplishment of this study, the following residues were used: wood processing residue (sawdust and planer shavings); coffee bean parchment and coffee plant stem; bean stem and pod; soybean stem and pod; rice husk; corn leaf, stem, straw and cob; and sugar cane straw and bagasse. For residue characterization the following analyses were done: chemical analysis, immediate chemical analysis, calorific value and elemental analysis. All procedures were conducted at the Laboratory of Forest Biomass Energy of the Federal University of Lavras. In general, all residues showed potential for energetic use. Rice husk was found to have higher lignin content, which is an interesting attribute as far as energy production is concerned. Its high ash content, however, led to a reduction in calorific value and fixed carbon. The remaining residues were found to have similar energetic characteristics, with corn cob showing greater calorific value, followed by coffee plant stem, both also containing higher levels of carbon and fixed carbon. A high correlation was found of higher calorific value with volatile materials, carbon and hydrogen contents.

Neste trabalho, apresenta-se um novo material adsorvente, obtido a partir da pirólise de resíduos da erva-mate. O carvão resultante demonstrou elevada área superficial específica quando comparado com outros materiais pirolisados e elevada capacidade de remoção de contaminantes orgânicos de soluções aquosas. Os valores de área específica apresentados pelos materiais foram de 344, 191 e ~0,5 m² g-1, para o carvão Mate 1, Mate 2 e Mate 3, respectivamente. As isotermas de adsorção mostraram que os carvões apresentam potencial para utilização como adsorvente para compostos orgânicos, tais como: o corante têxtil vermelho reativo, o corante azul de metileno e para o herbicida atrazina, sendo que os máximos de adsorção utilizando o carvão Mate 1 foram de 16, 230 e 30 mg g-1, respectivamente.

In this work we present a new adsorbent material, obtained by maté waste pyrolisis. The resulting charcoal presented high specific area when compared with other pyrolized materials and also high capacity to remove organic contaminants from aqueous solution. The charcoal showed specific area of 344, 191 and ~0.3 m² g-1 for sample Mate 1, Mate 2 and Mate 3, respectively. According to the corresponding adsorption isotherm these materials present good adsorption capacity for reactive textile and methylene blue dyes and the herbicide atrazine. Adsorption maxima were respectively 16, 230 and 35 mg g-1 for such substances, when sample Mate 1 was used.